ASTM D955-08 PDF

Scope: Mold shrinkage is the shrinkage of the polymer as it cools after the molding process. It is typically used to properly machine injection molds so that final. Purchase your copy of ASTM D – 08() as a PDF download or hard copy directly from the official BSI Shop. All BSI British Standards. Buy ASTM D R TEST METHOD OF MEASURING SHRINKAGE FROM MOLD DIMENSIONS OF THERMOPLASTICS from SAI.

Author: Arashira Tygojind
Country: Guinea
Language: English (Spanish)
Genre: History
Published (Last): 7 October 2010
Pages: 125
PDF File Size: 14.75 Mb
ePub File Size: 9.41 Mb
ISBN: 807-9-66631-468-7
Downloads: 3154
Price: Free* [*Free Regsitration Required]
Uploader: Morr

D — 08 Standard Test Method of Measuring Shrinkage from Mold Dimensions of Thermoplastics1 This standard is issued under the xed designation D ; the number immediately following the designation indicates the year of original adoption or, in the case of revision, the year of last revision.

A number in parentheses indicates the d95-508 of last reapproval. A superscript epsilon indicates an editorial change since the last revision or reapproval. Differences in mold shrinkage may also be observed among the three specimen geometries described in this test method.

The values given in parentheses are given for information only. It is the responsibility of the user atsm this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. Determination of Moulding Shrinkage 3. Current edition approved Nov. Originally approved in Last previous edition approved in as D – Summary of Test Method 4.

Signicance and Use 5. Factors such as mold and melt temperature, ll times, and packing conditions are known to affect shrinkage signicantly. Adherence to the specied mold design see 7. Factors, such as the amount of material in charge, cooling time, and pressure application are known to affect shrinkage signicantly. For example, thermoplastics, which absorb moisture must be dried before molding. The preparation given to the material prior to molding shall be recorded and reported.

Pressure transducers for monitoring the pressure in at least one cavity are mandatory for Type D2. Pressure transducers are recommended, but not mandatory for specimens Type A and Type B.

NOTE 2—Although scribe marks d95-08 not required, if they are used for injection or compression molded specimens for the measurement of shrinkage, the scribe marks shall be 1. NOTE 3—If the injection machines of appropriate capacity are not available, the requirements of 7. Orientation effects due to ow direction do not generally pertain to compression molding. The thickness shall be 3. The mold shall have at one end a gate 6.


NOTE 4—Although this specimen may be used to determine mold shrinkage in both the ow and cross ow directions, the astmm pattern does not produce uniform ow lengths and orientation.

Consequently, there may be signicant differences when measuring the specimen at different points around the circumference.

ASTM D – 08 Standard Test Method of Measuring Shrinkage from Mold Dimensions of Thermoplastics

Values would not be expected to be in agreement with those obtained using the specimens described in 8. Record these values as l and w, respectively. Three percent warp is dened as d9555-08 mm depth deection, positive or negative, per mm in length. The temperature of the heating cylinder and the mold shall be maintained at a point which, on a cycle selected, will produce temperature within the range recommended by the material molding standard.

Begin with a short shot to ensure the ow front is straight and not radial and that the ow is laminar and does not exhibit melt fracture jetting.

ASTM D955:08(2014)

Collect samples after the machine is at equilibrium. Do not modify or alter the edges used for the measurement of dimensions.

It is recommended to cool specimens in a horizontal position at room temperature by placing them on a material of low thermal conductivity to minimize warpage. Calculation and Report Report mold shrinkage in both ow and cross direction to two signicant gures. Precision and Bias Each material was supplied in granular form to each of the testing laboratories by a single supplier. Each test result is the average of ve individual determinations from successive injection molding cycles.

Each laboratory obtained one test d955-08 for each material. The results, including suggested cavity hold pressure for various materials, are shown in Appendix X1. Poorer precision larger values of Sr and r would be expected if the same operator were to shutdown and then restart the injection molding machine on the same day with the same mold, material and operating set points.

Repeatability under such circumstances was not evaluated. The data in Tables should not be rigorously applied to acceptance or rejected of material, as those d95508 are specic to the round robin and may not be representative of other lots, conditions, materials, or laboratories.

Users of this test method should d9955-08 the principles outlined in Practice E to generate data specic to their laboratory and materials, or between specic laboratories. The principles of Aatm would be incorrect to assume values form Tables for any new material. It is the intent of this method to control and document as many of these variables as possible. There are no recognized standards by which to estimate the bias of this test method. Intermediate values may also be used, however.


Thus the mass of material injected into the cavity is not clearly dened and the orientation of the material near the gate will be perturbed. Due f955-08 the inertia of the injection-molding machine, the effective change-over time is longer than its nominal value.

The correct change-over point shall therefore be adjusted 9d55-08 for each value of the injection speed and for each material under test. The decrease in the cavity pressure at hold to zero indicates that the material in the gate has solidied sufficiently to stop ow into the cavity. As c955-08 cooling rate of the material is proportional to the square of the reciprocal of the thickness, the minimum cooling time for the cavity can be expected to be close to 1.

At point R, the value of the cav ity pressure at hold is recorded. The minimum hold time can be read from the decrease of the cavity pressure to zero. November 1, 1 Completed ve year review. ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentioned in this standard.

Users of this standard are expressly advised that determination of the validity of any such patent rights, and the risk of infringement of such rights, are entirely their own responsibility. This standard is subject to revision at axtm time by the responsible technical committee and must be reviewed every ve years and if not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standards and should be addressed to ASTM International Headquarters.

Your comments will receive careful consideration at a meeting of the responsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you should make your views known to the ASTM Committee on Standards, at the address shown below.

Individual reprints single or multiple copies of this standard may be obtained by contacting ASTM at d95-08 above address or at phonefaxor service astm.